Usability of Natural Zeolites as Ceramic Pigments

Yıl 2014, Cilt: 14 Sayı: 3, 213 - 218, 01.12.2014

Eda Tasci Nihal Derin Coşkun Keriman Pekkan Veli Uz

Öz

Inthisstudy; thenaturalzeolite mineral which has ionexchangeandobsorptionproperties has hold in FeCl salt withdifferenttimesandabsorptionedtozeolitestructuresothismechanism has investigatedforusing as pigment. Thezeolitesampleswhich has waited in thesolution in differenttimes has prepared in differenttemperatureswith a calcinationoperationandused in transparentglaze. Theresults has shownthatforthe Fe element’senteringtozeolitestructure, 48 hours time is adequate and after this sample scalcination processan dusingin the glaze, prefercolourvalues has determined.© Afyon Kocatepe Üniversitesi 1. Giriş Seramik endüstrisinde sırları renklendirmek için inorganik seramik pigmentler kullanılmaktadır. Camsı matris içerisinde renk elde etmenin yolu çözünmeyen renkli kristal yapıya sahip olan pigmentleri matris içerisinde dağıtmaktır. Dağıtılan kristal pigmentin rengi transparan matrise geçerek sıra renk kazandırır (Özel and Turan, 2003). İnorganik pigmentler metal oksitler veya metal oksit içeren hammaddelerin karıştırılarak, yüksek sıcaklıklarda geçirilmesi ile elde edilen sentetik minerallerdir. İnorganik seramik pigmentlerin, termal kararlılık, sır içerisinde çözünmezlik, kimyasal bileşenlerin (asit ve bazların) etkisine dayanım, sır yüzeyinde hatalara yol açan gaz çıkışına neden olmaması gibi özelliklere sahip olması beklenmektedir

Anahtar Kelimeler

‘’Zeolit’’ ‘’Ceramic pigment’’ ‘’Wall tile’’ ‘’Glaze’’

Kaynakça

  • Mottana, R. Crespi, G. Liborio,1978. Guide to Rocks and Minerals, Simon and Schuster Inc., New York.
  • Baran, E., 2012. Tekli ve ikili sistemde zeolit yüzeyine malachitegreen adsorbsiyonunun araştırılması. Kilis Üni. FBE YL. Tezi.
  • Bondioli F., Andreola F., Barbieri L., Manfredini T. and Ferrari A. M. 2007. Effect of rice husk ash (RHA) in the synthesis of (Pr,Zr)SiO4 ceramic pigment. J. European Cer. Soc.27, 3483–3488.
  • Han, in: D.W. Ming, F.A. Mumpton (Eds.), Natural Zeolites ’93, 1995, Occurrence, Properties, Use, ICNZ, Brockport, New York, 421.
  • Pecsi-Donath, G. Nagy, in: D. Kallo, H. Sherry (Eds.), Occurrence, 1988. Properties and Utilization of Natural Zeolites,AcadeKiado, Budapest, 291.
  • Eppler, A., R., 2000. Glazesfor High-Fire Bodies. Cer. Eng. Sci. andProc.,21, 2.
  • Rodriguez-Fuentes, C. Lariot Sanchez, J.C. Romero, R. Roque-Malherbe, in: B.Drzaj, S. Hocevar, S. Pejovnik (Eds.), Structure,Technology and Application, Ljubljana, 375. – Synthesis,
  • Hill, K.,Lehman, R., Swiler, D., 2008. TheEffect of SelectedProcessingVariables on ColorFormation in Praseodymium-DopedZirconPigments. CeramicEng. andSci. Proc.,21, 2.
  • ItalianCeramicSociety, 2003. Colour, pigmentsandcolouring in ceramics. SALA, Modena. Pishch,
  • G.N.Maslennikova, K.B. Podbolotov, Yu.A.Kariznaand
  • I.V.Belyakovich,2011.SilicaBasedPigments. 68, (3-4), 71-75)
  • Stelzer, M. Paulus, M. Hunger, J. 1998. Weitkamp, Mic. Mesoporous Mat. 22 ,1.
  • Joshi, V.V. Joshi, A.L. Choudhari, M.W. Kasture, 1997, Materials Chemical Physics. 48 ,160.
  • Ozel, E., Turan, S., 2003. Production and Characterisation of Iron-Chromium Pigments and Their Interactions with Transparent Glazes. J. European Cer. Soc.,23, 2097-2104.
  • Lewis, Pigment Handbook, 1988. Properties and Economics.2nd Ed., John Wiley & Sons, New York, USA, 1, 945.
  • Tekbaş, M., 2007. Fe+3 ile modifiye edilmiş zeolit katalizi ile azo boya çözeltisinin foto oksidasyonu. GYTE, FBE YL. Tezi, Çevre Mühendisliği A.B.D.
  • Pogrebenkov and M. B. Sedelnikova, 2002.
  • CeramicPigmentsBased on Natural Minerals, Glass
  • and Ceramics, 59 ( 11-12), 396-399.
  • Pogrebenkov, M. B. Sedelnikova and V. I. Vereshchagin, 1998. Zeolites: Rawmaterialforceramicpigments, Glass and Ceramics,55 (1-2), 55-56. İnternet kaynakları
  • www.akvaryum.com., (08.09.2012)
  • www.koruma.com\demir3klorür (08.09.2012)
  • www.wikipedia.com\zeolit., (09.09.2012)

Doğal Zeolitlerin Seramik Pigment Olarak Kullanılabilirliği

Yıl 2014, Cilt: 14 Sayı: 3, 213 - 218, 01.12.2014

Eda Tasci Nihal Derin Coşkun Keriman Pekkan Veli Uz

Öz

Bu çalışmada; iyon değişimi ve absorbsiyon yapabilme özelliği olan doğal zeolit minerali FeCl+3 tuzu çözeltisi içerisinde farklı sürelerde tutularak demirin zeolit yapısına absorbsiyonu sağlanarak pigment olarak üretilebilirliği araştırılmıştır. Farklı sürelerde çözelti içerisinde bekletilen zeolit örnekleri farklı sıcaklıklarda kalsine edilerek hazırlanmış ve bu örnekler transparan sırda kullanılmıştır. Elde edilen sonuçlarda 48 saatlik sürenin demirin zeolit yapısına girmesi için yeterli olduğu ve bu örneklerin kalsine edilmesi sonrasında ve sırda en iyi renk değerlerini verdiği belirlenmiştir Usability of Natural Zeolites as Ceramic Pigments

Anahtar Kelimeler

“Zeolit”; “Seramik pigment”; “Duvar karosu ”; ‘’Sır’’

Kaynakça

  • Mottana, R. Crespi, G. Liborio,1978. Guide to Rocks and Minerals, Simon and Schuster Inc., New York.
  • Baran, E., 2012. Tekli ve ikili sistemde zeolit yüzeyine malachitegreen adsorbsiyonunun araştırılması. Kilis Üni. FBE YL. Tezi.
  • Bondioli F., Andreola F., Barbieri L., Manfredini T. and Ferrari A. M. 2007. Effect of rice husk ash (RHA) in the synthesis of (Pr,Zr)SiO4 ceramic pigment. J. European Cer. Soc.27, 3483–3488.
  • Han, in: D.W. Ming, F.A. Mumpton (Eds.), Natural Zeolites ’93, 1995, Occurrence, Properties, Use, ICNZ, Brockport, New York, 421.
  • Pecsi-Donath, G. Nagy, in: D. Kallo, H. Sherry (Eds.), Occurrence, 1988. Properties and Utilization of Natural Zeolites,AcadeKiado, Budapest, 291.
  • Eppler, A., R., 2000. Glazesfor High-Fire Bodies. Cer. Eng. Sci. andProc.,21, 2.
  • Rodriguez-Fuentes, C. Lariot Sanchez, J.C. Romero, R. Roque-Malherbe, in: B.Drzaj, S. Hocevar, S. Pejovnik (Eds.), Structure,Technology and Application, Ljubljana, 375. – Synthesis,
  • Hill, K.,Lehman, R., Swiler, D., 2008. TheEffect of SelectedProcessingVariables on ColorFormation in Praseodymium-DopedZirconPigments. CeramicEng. andSci. Proc.,21, 2.
  • ItalianCeramicSociety, 2003. Colour, pigmentsandcolouring in ceramics. SALA, Modena. Pishch,
  • G.N.Maslennikova, K.B. Podbolotov, Yu.A.Kariznaand
  • I.V.Belyakovich,2011.SilicaBasedPigments. 68, (3-4), 71-75)
  • Stelzer, M. Paulus, M. Hunger, J. 1998. Weitkamp, Mic. Mesoporous Mat. 22 ,1.
  • Joshi, V.V. Joshi, A.L. Choudhari, M.W. Kasture, 1997, Materials Chemical Physics. 48 ,160.
  • Ozel, E., Turan, S., 2003. Production and Characterisation of Iron-Chromium Pigments and Their Interactions with Transparent Glazes. J. European Cer. Soc.,23, 2097-2104.
  • Lewis, Pigment Handbook, 1988. Properties and Economics.2nd Ed., John Wiley & Sons, New York, USA, 1, 945.
  • Tekbaş, M., 2007. Fe+3 ile modifiye edilmiş zeolit katalizi ile azo boya çözeltisinin foto oksidasyonu. GYTE, FBE YL. Tezi, Çevre Mühendisliği A.B.D.
  • Pogrebenkov and M. B. Sedelnikova, 2002.
  • CeramicPigmentsBased on Natural Minerals, Glass
  • and Ceramics, 59 ( 11-12), 396-399.
  • Pogrebenkov, M. B. Sedelnikova and V. I. Vereshchagin, 1998. Zeolites: Rawmaterialforceramicpigments, Glass and Ceramics,55 (1-2), 55-56. İnternet kaynakları
  • www.akvaryum.com., (08.09.2012)
  • www.koruma.com\demir3klorür (08.09.2012)
  • www.wikipedia.com\zeolit., (09.09.2012)
Toplam 23 adet kaynakça vardır.

Ayrıntılar

Birincil Dil Türkçe
Bölüm Makaleler
Yazarlar

Eda Tasci Bu kişi benim

Nihal Derin Coşkun

Keriman Pekkan Bu kişi benim

Veli Uz Bu kişi benim

Yayımlanma Tarihi 1 Aralık 2014
Gönderilme Tarihi 8 Ağustos 2015
Yayımlandığı Sayı Yıl 2014 Cilt: 14 Sayı: 3

Kaynak Göster

APA Tasci, E., Coşkun, N. D., Pekkan, K., Uz, V. (2014). Doğal Zeolitlerin Seramik Pigment Olarak Kullanılabilirliği. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi, 14(3), 213-218.
AMA Tasci E, Coşkun ND, Pekkan K, Uz V. Doğal Zeolitlerin Seramik Pigment Olarak Kullanılabilirliği. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi. Aralık 2014;14(3):213-218.
Chicago Tasci, Eda, Nihal Derin Coşkun, Keriman Pekkan, ve Veli Uz. “Doğal Zeolitlerin Seramik Pigment Olarak Kullanılabilirliği”. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi 14, sy. 3 (Aralık 2014): 213-18.
EndNote Tasci E, Coşkun ND, Pekkan K, Uz V (01 Aralık 2014) Doğal Zeolitlerin Seramik Pigment Olarak Kullanılabilirliği. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi 14 3 213–218.
IEEE E. Tasci, N. D. Coşkun, K. Pekkan, ve V. Uz, “Doğal Zeolitlerin Seramik Pigment Olarak Kullanılabilirliği”, Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi, c. 14, sy. 3, ss. 213–218, 2014.
ISNAD Tasci, Eda vd. “Doğal Zeolitlerin Seramik Pigment Olarak Kullanılabilirliği”. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi 14/3 (Aralık 2014), 213-218.
JAMA Tasci E, Coşkun ND, Pekkan K, Uz V. Doğal Zeolitlerin Seramik Pigment Olarak Kullanılabilirliği. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi. 2014;14:213–218.
MLA Tasci, Eda vd. “Doğal Zeolitlerin Seramik Pigment Olarak Kullanılabilirliği”. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi, c. 14, sy. 3, 2014, ss. 213-8.
Vancouver Tasci E, Coşkun ND, Pekkan K, Uz V. Doğal Zeolitlerin Seramik Pigment Olarak Kullanılabilirliği. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi. 2014;14(3):213-8.